SNM8055 medium and high temperature sintered conductive silver paste is made from ultrafine silver powder, medium and high temperature glass powder and carrier. This product can be adapted to glass-ceramics, ceramic bases, atomizing sheets, etc. High-conductivity circuits can be obtained by screen printing, drying and sintering (550 ~ 700 ºC). Has excellent adhesion, high solder resistance, and excellent electrical properties. After sintering, the silver surface is bright and dense, with good continuity and strong oxidation resistance. Inorganic fillers do not contain heavy metals such as lead, chromium, mercury, and hexavalent chromium, and comply with EU RoHS environmental protection requirements.

Technical Index
Application Condition

1. Stirring: After refrigerating, the silver paste should be returned to room temperature (25 ° C), and then used after stirring for 10 minutes.
2. Printing: In a clean and well-ventilated environment, it is recommended that the screen mesh number is 150-325 mesh and the latex thickness is 5-25 μm.
3. Curing: Infrared tunnel furnace 200 ºC & 5min.
4. 4. Cleaning: It is recommended to use net water for cleaning.
5. Dilution: The viscosity of the slurry can be adjusted with a special thinner to suit the process requirements. However, it is generally not recommended for use, and new pulp does not need to be adjusted.
6. Transportation and storage: During transportation and storage, the product should be protected from moisture, pollution, and high temperature; it should be stored in a clean, dry, and open flame environment. The best temperature for storage is 5-25 degrees, and it should be protected from sunlight Direct shot. The shelf life of the slurry is 6 months.